Here it is all cleaned up. I was really discouraged to find cracks along the spine and the tang which I assume are from the heat treating process. The cracks were not apparent under the black corrosion. Some of the pitting was scary deep but it cleaned up. I left some pitting around the makers stamp. I have seen these type of cracks in the past on some Sheffield wedges. I do not recall them mentioned in the forums. Can any with more knowledge then me chime in? I expect it will shave well, just not the thing of beauty I'd hoped for.
Attachment 194206Attachment 194207Attachment 194208