correct me if I'm wrong, but does not Mr Zowada make his steels from scratch on occasion?
Printable View
correct me if I'm wrong, but does not Mr Zowada make his steels from scratch on occasion?
As have I, for a decade or so.
Here is my take on this subject ! Most blade smiths (people who forge blades) pay quite a lot of attention to grain refinement in the steels they use , mainly because in the forging process there is quite a bit of grain growth . On that same token , most people who do stock removal (grinding away steel to create the shape of the blade) just assume that the steel they buy is already in a state of fine grain ! This is not always the case !!! But taking this as a rule , the bladesmiths will generally end up with a finer grain steel and the finer the grain in the steel , the better the blade will perform (that is an absolute fact) . That all said , there are guys out there that will go the extra mile to ensure they get the best result possible no matter what process they follow . I personally to mostly stock removal as most of my razors are stainless (RWL34) and i have spent a lot of money and a lot of time to refine my heat treatment process to get the best results i possibly can . This includes a full soft anneal and spheridize (where needed) and a sub zero quench (taking the steel down to minus 80°c after the initial quench ! With the older technology steels like the 10xx series and W series steels , this is of critical importance , where as with some of the modern steels you do not need to pay anywhere near as much attention with it . Some of the more modern steels are superior to the older steels in just about every way , but this does not mean that the knives made from them are better than the old steels , it just means that they will perform better if they are treated correctly !
As for forged blades being better than stock removed blades , i do think that is a myth , provided they have both had the same attention payed on them ! This may be a whole big can of worms , but having spent many hundreds of hours going through the motions and doing tests and reading what other have done and having done a degree in metallurgy, i honestly believe this to be the case !
Correct RazorJack. If you start with good steel and treat it correctly, it will produce a good tool regardless of forged or stock removal. Also, if you start with good steel and treat it poorly, you will end up with a poor performing tool. I'd rather have a knife or razor that was made from 1050 and heat treated correctly, than a knife or razor made from the latest and greatest steel that was improperly heat treated.
As I've said in the past, I forge because the steel that I like to use is in the wrong shape and stock removal isn't an option. I'm also a big believer in the correct steel for the tool. My favorite hunting knife steel would make a pretty terrible razor.