New kid on the block :P

I'm just happy:rock:,,,,want to share this with you:rock:. Hope i'm patient until this arrives :angel:.



I present to you.. Mr reynolds (not burt).Horn scales,, 7/8.. what should i do about the water spots??

Try some Maas, but I have a feeling she'd need sanding to get those stains out. I hope that pitting by the edge isn't problematic, but I fear it will be...

When you get it try setting the bevel and see if the pitting is going to give you a swiss cheese edge before you invest a lot of time in sanding the spots. If it was mine, once I found the pitting at the bevel didn't go far and I could get to good steel, I would just Semichrome it with a paper towel and live with the spots. :shrug:

the seller confirms it to be water spots and not rust:shrug:

Quote:

---

Originally Posted by ri7ani

the seller confirms it to be water spots and not rust:shrug:

---

Cool try the Maas or whatever metal polish on a paper towel. Personally I just don't have the patience and fortitude to hand sand of hours and would rather live with a bit of patina. YMMV. :)

Semichrome it with a paper towel??????? you mean polishing???

Semichrome, Maas, Flitz... if the spots are a little stubborn, try just a dab of one of these polishes with a little piece of #2500 wet/dry sandpaper. It will give you a good idea where you stand without much time, effort, or destruction.

Quote:

---

Originally Posted by ri7ani

the seller confirms it to be water spots and not rust:shrug:

---

If you define rust as red stuff, no, clearly there is none. But clearly there is staining and pitting. Pitting is where corrosion ate away at the metal; it can usually be found under rust. Perhaps there was once rust on that blade, or perhaps something else caused the pitting.

Rust, if it is present, is easy to get rid of; it can be scraped right off or removed with some metal polish. It's the pitting underneath that is the real problem.

Quote:

---

Originally Posted by holli4pirating

If you define rust as red stuff, no, clearly there is none. But clearly there is staining and pitting. Pitting is where corrosion ate away at the metal; it can usually be found under rust. Perhaps there was once rust on that blade, or perhaps something else caused the pitting.

Rust, if it is present, is easy to get rid of; it can be scraped right off or removed with some metal polish. It's the pitting underneath that is the real problem.

---

Dylan -- did you want to leap in and spend a few days honing that one?

Nice looking razor.

I should be receiving the razor any day now,,,but i wont hone it until june or july since i will be rescaling all 9 of my razors....but once i start honing i will make sure to tell you guys how it went....worse case scenario i'll bring to 6/8 instead of 7/8 :P