Some experimenting

Quick backstory:
I love all things gaudy when it comes to cars and motorcycles, like heavy metal flake paints, lots of gold and brass, etc. Picture a lime green with gold flake Impala and gold Daytons.
So naturally I want to make a brush like that but my search for glitter acrylics or other materials came up short. Found one place but they said they weren't running any rods at the time.
So I bought some polyester resin for casting and did some mixing. Playing with the amount of hardener takes some time and also suspending the glitter. Too little hardener and it's tacky or scratches, and too much and it creates too much heat and cracks. Some of you may already know this process but new to me.
Below are some pictures from casting to turning.
The most difficult part is turning for me - as you can see the shape is simple cause it's very brittle and my tools would catch easily. I need major practice there. Comments welcome! I'm pretty pleased with this one but even more I'm excited at the possibilities with what you can do.

Attachment 171287
Attachment 171288
Attachment 171289
Attachment 171290
Attachment 171291
Attachment 171292
Attachment 171293

Well done.
Cannot advise as i have not done this, but congratulations for having a lash and especially for succeeding!

Thats Neat.I rarley turn phenolics but have found that spindle speed is critical.About 1700 seems to be the sweet spot.

Quote:

---

Originally Posted by Adam G.

Well done.
Cannot advise as i have not done this, but congratulations for having a lash and especially for succeeding!

---

Thanks! I almost forgot I posted this it was so quiet :)
I did a couple more castings and got one to come out much more transparent. When I clean it up I'll post a pic.

Quote:

---

Originally Posted by pixelfixed

Thats Neat.I rarley turn phenolics but have found that spindle speed is critical.About 1700 seems to be the sweet spot.

---

It's interesting you say that cause in my research today I basically found out I need to be turning faster. I also ordered one of the carbide tools from the site you suggested Bill. Can't wait to get it...

Quote:

---

Originally Posted by RoyalCake

It's interesting you say that cause in my research today I basically found out I need to be turning faster. I also ordered one of the carbide tools from the site you suggested Bill. Can't wait to get it...

---

So many diff types of phenolics,I have only turned delrin and plexi.

Funny you say 1700 rpm. That's my go to speed for turning.

You turn by hand? I would try "riding the bevel" with this material. It creates more of a shearing cut rather than a scraping cut. Less chance of a piece breaking off or chipping. It's a technique used to achieve very smooth cuts.

Riding the Bevel - NewWoodworker.com LLC

I should add that I like what your doing here. If you come away with good results, I might try it. Looks like fun.

Quote:

---

Originally Posted by HARRYWALLY

Funny you say 1700 rpm. That's my go to speed for turning.

You turn by hand? I would try "riding the bevel" with this material. It creates more of a shearing cut rather than a scraping cut. Less chance of a piece breaking off or chipping. It's a technique used to achieve very smooth cuts.

Riding the Bevel - NewWoodworker.com LLC

---

Thanks for the link! I knew the term but never read the detailed explanation.
The amber one I cast last night seems much better (glad I didn't glue the knot in yet). When I get the surface cleaned up I'll post a pic.
Yeah I'm excited about the possibilities.

All great stuff guys,you can buy zillions of extruded handles (all made in China) I love the home brew you guys are doing.one of a kind stuff.