Frankensteel razor #1
The story of this little project has kind of been split between two threads up until now, so I figured it made sense to bring it together here.
Long story short, a question was asked a while back about whether anyone had tried melting down and re-using steel from vintage Sheffield blades. I don't have any kind of smelting experience or equipment, so that was well beyond my scope, but it got me thinking that it should be possible to forge weld together a billet made up of vintage blades. Since I had a small pile of blades that were, for a variety of reasons, beyond salvation, I decided to give it a shot.
These are the blades: there's a W&B FBU ( honed beyond recognition, poor thing ), a DD, couple Joseph Allens, a Boker, and a bunch of random others. So I strayed from the original idea in that they're not all Sheffield blades, but they are all vintage 19th/early 20th century blades. I rejected one of the blades as I didn't like the way it sparked when I was grinding it, so ended using 11 of the original 12.
Attachment 280179
I flattened the spine and tail, ground off the blades (which were essentially foil & scale at this point), and cut them off at the pin hole to avoid cold shuts.
Attachment 280181
Then stacked them, welded the billet ends, and got the forge nice and hot
Attachment 280180
They forge welded *really* nicely and so I ended up with an 11-layer billet of vintage razor steel.
Attachment 280182
-
Ok you crazy guy! You have my attention.........
-
4 Attachment(s)
I was really impressed with how well the steel welded. At least the first weld. My decision to fold it and double the layer count will come back to haunt me...
But the result was a nice solid billet
Attachment 280183
This turned into a vaguely RSO
Attachment 280184
Before this, I had only tried to make one razor, and I screwed that one up by getting it too hot grinding, resulting in a crack. So I'm determined to take this one as slow and easy as possible. Less grinder work, and more hand sanding was the idea.
Attachment 280185
A crap ton of wet/dry and two sore hands later, it was getting pretty close to what I wanted: big and with a nice heavy grind
Attachment 280186
-
Beautiful - send it to me when you're done, you know I crave Sheffield steel....great job, and I bow and defer to your efforts in stepping into the Time Machine.....:beer1:
-
1 Attachment(s)
Now all you need is the famous FrankenPhig. :shrug:
Attachment 280189
-
5 Attachment(s)
And this is where the decision to fold the billet came back to bite. About 2/3 of the way to the toe, you can see that there's a bad weld. It's on the side, and not right on the edge, so not a total disaster, but not good. The good news is that it survived hardening. The bad news is that the bad weld looked much worse after tempering.
Attachment 280187
And then, when going to do the final grind... disaster! Or, potential disaster... The bad weld extended way, way further back into the billet than I had hoped.
Attachment 280188
So... back to the grinder, and plan B. No more heavy grind for this razor unfortunately. As I chased the bad weld back in search of solid steel, the grind got lighter, and lighter, and lighter. This all was making me very nervous because a) I have no proper tools for hollow grinds b) I have no experience doing hollow grinds, and c) by this point, I really just want to get at least one shave out of this thing!
Attachment 280190
So the dodgy weld got smaller, the blade got thinner, and I got more nervous. And this is where I stopped for the night.
Attachment 280191
Remember when I was aiming for a heavy grind? Looks like I'm heading for a completely unintentional kamisori grind on this guy. This is turning into a really strange razor... but it ain't dead yet!
Attachment 280193
-
I like it the way it is, shows character.
Frankenstein himself had a lot of scars. :tu
-
Throw some JB Weld in there and call it a day! It's a thing of beauty!
-
I mean, the key question is, will it shave?
https://www.youtube.com/watch?v=5XNSKIzDPtg
-
The ultimate restoration!