i accidentally started to final grind a blade when i realized that i hadn't done the heat treatment on it done hahaha right now the thickenss of the edge is down to .5mm thick, it is a wedge so its not .05mm for half the blade so i think i might be in luck... i have never heat treated a blade this thin before and when i was thinking about it i figured that the edge was going to heat up a heck of a lot faster than the spine, so to reduce stress i thought about having the soak time being really short... aside from that i really cannot think of anything else i should do different on this blade.

i have once heard of someone at charlies get together HT a blade that was really thin and kind of remember the person saying they were successful at it..

the blade is san mai, 1095 core, nickel shim(dont think the nickel matters) with mild steel cladding...

thanks in advance gents