Looks like near wedge to me from previous thread. Post some photos of the whole blade, not just the profile, would help. An hour on a DMT 1200?
Printable View
Looks like near wedge to me from previous thread. Post some photos of the whole blade, not just the profile, would help. An hour on a DMT 1200?
i did exactly the same on it, it had a big crack on the bevel so i did not have any other choice than this procedure. the blade has no smile, it is fine and plane with no cracks or micro crack in the bevel.
to answer about other coms, with 3 or 8 layers, it's only the hone wear touch on the stone and not the bevel. i ask myself if the blade lost too much larger of its and to put it on action, will i need to grind it? because in this way, as i said before the hone wear does not touch the bevel on the hone.
for pictures, i will try to do them this afternoon, otherwise i could only tomorrow night.
If I am reading this right, the hone is only touching/working on the shoulder of the bevel and not reaching to the edge even with excessive layers of tape on the spine. I almost think that the blade may be way out in geometry. Sounds like the spine is way too narrow for the width of the blade as it now is.
What is the spine width in mm and width of the blade measured from where the spine contacts the hone to the edge in mm?
Bob
here some pics,
just marked the edge with black pen
Attachment 222344Attachment 222345
and here, after few passes on 400 grit. as you see there is fine draw, the black mark is gone. but below this line, there is the bevel which does not touch to hone.
Attachment 222346
i think when i corrected the crack (about 1.5 mm) the blade lost a lot of his large. i think i just need to regrind it (well i don't have grinder) or continue on DMT because the edge is still not enough fine to have a bevel.
that's the only explanation i can get.
Yes, I do think from those measurements that the spine is far too narrow for the blade width as it is now. I think for a 20mm blade the spine should be 5mm to 5.5mm wide to get a good bevel angle. A 4mm wide spine should be for a 14mm wide blade to get a good bevel angle.
I am not an expert and do not know a solution to the problem. I am sure more knowledgeable members of the forum may be able to help.
Bob
I think you are getting that bevel because you were grinding on it with 20 layers of tape. Now you're trying with a few layers and it's going to take a whole lot of work to get that thing set. Did you try to "bread knife" this blade befor honing?
as i said earlier yes i tried butter knife when i deleted the crack
well i found a solution, as i said this was a 7/8 wedge with a big crack (almost 2 mm) in the bevel which i corrected. but here is the problem, at least, as the blade lost of largeness there is a inequality to remake the bevel, it must to be regrinded to have a correct bevel.
well i don't have one of these machines. the only way i can, is the lift the spine with some degree for the bevel work on the hone. i just discovered this. the bevel is much better, unless i have a big hone wear which i will need to clean and rehone the blade.
here, there is a picture i made for explain better what i'm talking about;
Attachment 222373
the red line for show how i shorted the blade for correct the bevel and clean the crack. the blue lines shows the new bevel which can be done without regrind the blade.
if you have ony other idea for this case, share it please.
merry christmas to all