I need a metal remover- 220 or 400

[khaos]

So the title pretty much sums it up. I would be grabbing a Naniwa stone because I am very pleased with my current ones. I was wondering though, would a 220 or a 400 be more useful? I currently need one because I have a razor that is so close to a full wedge (2/3's of it is hone wear) that I just wanna go the whole way, but it swarf's up the 1k so fast it takes for ever. Obviously for this I'd want the 220, but down the road, which would be more useful?

Thanks!

[holli4pirating]

I've used a Norton 220 at JoeD's place; it was very helpful when honing up my 9/8 Greaves. I would recommend it without any hesitation... or as little hesitation as possible seeing as I only spend a few hours using it. Really all I can say is, for me and that razor, the Norton 220 was great.

[khaos]

Actually... if I got a DMT Coarse, would that work? Then it could do double duty lapping hones.

[Memorael]

I personally would go with the shapton gs in 220, fast flat convenient what more could you want? The dmt's are waaaay to aggressive IMO

[JimmyHAD]

Actually... if I got a DMT Coarse, would that work? Then it could do double duty lapping hones.

That has worked well for me. It ain't 220 but it is close enough for the amount of times that I've needed to go that coarse. Worth a try and then if you find you need to go for a coarser hone do so.

[Slartibartfast]

That has worked well for me. It ain't 220 but it is close enough for the amount of times that I've needed to go that coarse. Worth a try and then if you find you need to go for a coarser hone do so.

DMT's remove metal like nobody's business too...

[JimmyHAD]

DMT's remove metal like nobody's business too...

They sure do Ben. TBH the only time I have found the need to go as coarse as the 325 has been on a few Sheffield wedges and on a Hermes that had a bad frown and I had to restore the bevel after I breadknifed it. One of the fore mentioned wedges had a bad chip. Usually I've found the DMT 1200 plenty to do the initial bevel setting.

[kevint]

I've used Shapton pro, Norton, and King in the 120-220, because they wear down so quickly I went to diamond. At the time I did not think about how they also wear out but at least they hold their shape.

But a diasharp will not do very well at the shoulder. Atoma has a sharper corner, still not really an advantage but better than diasharp. (Haven't tried any other plates.) You will have to deal with the shoulder going to flat wedge, which is probably not the best idea, but I understand the urge.

Everything about stones is a compromise.

If you are looking at 3/8 thick nani- there probably is not a lot of future when grinding/shaping whole blade faces.

if you continually rotate 90 degrees every 5 or 10 strokes you can use the stone much more evenly. If you let it get too far out of whack, it will play hell trying to get scratches out on 1000>+