If it's a hardening line, I would expect it to be visible on both sides given the very thin cross section of the blade edge. More information and time will tell.

If this is carbon steel, it could be as simple as a hardening line. That is, about all of the blade that got hard during heat treatment. It seems to follow the edge. Better pictures would help. ...