Allow me to express doubt about your assertion. Bainite forms from austenite, not martensite, and requires very specific temperatures to achieve, including cooling rate, both of those are different...

Then what's different between the tempering cycles for martensite and bainite? All you've explained up to now is that bainite is a degradation structure between martensite and pearlite, not that...

Do you need to do this for every blade? The ABS spends a good deal of energy specifying a differentially hardened blade in their testing criteria. There are a lot of folks making Japanese style...

Find some firebricks to block up the exhaust hole and that little fire will retain a lot more heat. Really, any forge is nothing more than a collection of insulation to contain the heat in one spot...