Sadly, there is a phenomena called decarburization that can occur when the blade is being brought up to heat treatment temperature and allowed to soak too long in too hot a fire, like at the end of a...

It doesn't sound like a problem with the blade being hard enough because you would have noticed it abrading more during honing. Maybe a wire edge/angle issue?