02-25-2015, 05:05 PM
- Replies
- 76
- Views
- 7,267
Exactly. :)
Exactly. :)
-
02-24-2015, 07:07 AM
- Replies
- 76
- Views
- 7,267
Yes, it seems. I am happy with it. I will change...
Yes, it seems. I am happy with it. I will change my thermocouple and make a complete HT. I hope... :)
-
02-19-2015, 06:15 PM
- Replies
- 76
- Views
- 7,267
Sorry guys, I was stupid. I strongly trusted in...
Sorry guys, I was stupid. I strongly trusted in screen of the oven. This is a small oven with specialities like powerlessness. I have done some test, you can see below the result.
193820
A... -
02-13-2015, 10:14 PM
- Replies
- 76
- Views
- 7,267
No, not just mine HT. I bought my oven because I...
No, not just mine HT. I bought my oven because I want to keep everything in my hand. But it is also possible that I am overthinking this problem.
-
02-13-2015, 10:02 PM
- Replies
- 76
- Views
- 7,267
Yes, I understand this but I think there are...
Yes, I understand this but I think there are good/average edge and the perfect edge. I want to get the maximum from O1.
I am not satisfied with the current results. Not just with my own heat... -
02-13-2015, 07:18 PM
- Replies
- 76
- Views
- 7,267
Many thanks. Actually I understand why you worte...
Many thanks. Actually I understand why you worte the starting temperature should be 190C.
-
02-13-2015, 06:50 PM
- Replies
- 76
- Views
- 7,267
Thanks, Mike! I missed your answer and I am...
Thanks, Mike!
I missed your answer and I am tempering now. :)
I reduced my soaking time to around 9 minutes and with opening my oven' door I was able to reach at 798-805C. My tempering time 2x2h,... -
02-13-2015, 11:49 AM
- Replies
- 76
- Views
- 7,267
I also get the feeling. ;)
I also get the feeling. ;)
-
02-13-2015, 11:22 AM
- Replies
- 76
- Views
- 7,267
I made a couple of mini-razor for this purpose....
I made a couple of mini-razor for this purpose. These are not wellworked. I want to be good at the heat tempering.
193319
"How confident are you that your thermocouple is accurate?" - I dont... -
02-13-2015, 10:47 AM
- Replies
- 76
- Views
- 7,267
I finished the fourth attempt as well. Fourth...
I finished the fourth attempt as well.
Fourth attempt
edge 1 mm
normalizing: none
thermal cycling: 1472F (800C), three times, in 130F (55C) warm oil 2-3 sec.
soaking: 1472F (800C), 15 min.... -
02-11-2015, 07:42 PM
- Replies
- 76
- Views
- 7,267
Mike, I just read it more carefully. Maybe I used...
Mike, I just read it more carefully. Maybe I used the wrong term: normalizing.
This is my process from SRP's pdf:
"To normalize, I heat the steel to 1450 F, hold it there for a couple of... -
02-11-2015, 04:39 PM
- Replies
- 76
- Views
- 7,267
It is logical, thank you. If all goes well,...
It is logical, thank you. If all goes well, tomorrow or the day after tomorrow I will publish the fourth attempt...
-
02-11-2015, 11:10 AM
- Replies
- 76
- Views
- 7,267
One more question. And what about the Preheating...
One more question. And what about the Preheating Temperature: 1110-1290 ° F (600-700 ° C)? I ignored it so far.
-
02-10-2015, 09:47 PM
- Replies
- 76
- Views
- 7,267
Thanks, I see. And keep it just for a few seconds...
Thanks, I see. And keep it just for a few seconds in the warm oil?
-
02-10-2015, 09:15 PM
- Replies
- 76
- Views
- 7,267
Today I have made a new small razor for the next...
Today I have made a new small razor for the next attempt. :) How warm the oil would be?
This will be the next attempt. Thanks!
Your welcome.
Thank you so much! :) -
02-10-2015, 08:49 PM
- Replies
- 76
- Views
- 7,267
Maybe not, but I thought it could not hurt.
Maybe not, but I thought it could not hurt.
-
02-10-2015, 08:47 PM
- Replies
- 76
- Views
- 7,267
Many thanks for your useful advices. I will...
Many thanks for your useful advices. I will utilize them tomorrow. :)
I plan to use cryo treatment, but first I would like to make a really nice edge on traditional way. I am a perfectionist, I'm... -
02-10-2015, 08:32 PM
- Replies
- 76
- Views
- 7,267
:) Around 61 HRC. But more important for me...
:)
Around 61 HRC. But more important for me the fine and durable edge.
Thank you for your help! -
02-10-2015, 08:27 PM
- Replies
- 76
- Views
- 7,267
The 1,2,4 are the same bar and a third one is...
The 1,2,4 are the same bar and a third one is just from the same retailer.
During my normalization process I take out and then allowing it to cool slowly in still air as long as it will not be all... -
02-10-2015, 11:58 AM
- Replies
- 76
- Views
- 7,267
I made some pictures today. I hope to see the...
I made some pictures today. I hope to see the details.
First attempt
edge 0.5 mm
normalizing: 805C, 3 times
soaking: 805C, 15 min.
quenching oil: 80C, 5-10 sec
tempering: after cooling to... -
02-08-2015, 08:30 PM
- Replies
- 76
- Views
- 7,267
I learned more in two days than I ever thought I...
I learned more in two days than I ever thought I would. Thank you very much for all!
-
02-08-2015, 06:49 PM
- Replies
- 76
- Views
- 7,267
I broked some and I will take some pictures and...
I broked some and I will take some pictures and post them.
One more question: How many times can I re-HT a steel without significant loss?
And thank you very much for all these useful comments!... -
02-08-2015, 06:03 PM
- Replies
- 76
- Views
- 7,267
Thanks for the comment! Yes, I have. I have...
Thanks for the comment!
Yes, I have. I have broked one but more will follow. I grinded couple of razors just for tests.
Then it should be no problem. -
02-08-2015, 05:20 PM
- Replies
- 76
- Views
- 7,267
I dont use DMT. I hone wiht japanese synthetics...
I dont use DMT. I hone wiht japanese synthetics and naturals. I use loupe as well. Rather my fault is the "overhoning".
I see, thanks. -
02-08-2015, 04:36 PM
- Replies
- 76
- Views
- 7,267
Good idea, thanks! The hardness is...
Good idea, thanks! The hardness is enough(sometimes to hard :)), the sensitivity is my problem.