I can *totally* understand what you want, and I think it would be fantastic to won a razor that resulted from one's own input in this way.

But I'm not sure you have a firm grasp of the work...

Realized I forgot your other question: *final* shaping is after heat treatment.

What you want by the time you're heat treating is a razor-shaped object. I.e. your hole for the pin is drilled,...

Are you asking what you should pay for the steel? Or for heat treament?

I'm curious as to the choice of alloy. Azom lists the application for 52100 as "AISI 52100 alloy steel is used in bearings...