Wow, like I said I have never seen one that bad. If it is cell rot, quite likely is, a carbon blade might have been eaten up even more to the point of falling apart at a mere touch. Definitely not...

My guess would be that it would take a lot, far more than carbon steel, to get a stainless steel blade to that condition. Sure doable although I have not seen one that bad personally. I'd be...