The outline is the easy part and you can leave long whatever you choose so that you can make decisions as you go. Your still going to have to do some shaping and grinding after the cut and not to...

Cold stamp sounds the best for you buddy ! The only thing you have to worry about then is work hardening. Your material should come annealed or your not paying enough for it. And it sounds like your...

You can temper at about 400 degrees (depending on the steel ) but to normalize your going to have to get closer to critical or past it and hold for awhile. This should be done before or at heat...