Herr Schick really needs to reinstall the treadle on his air hammer. :D

LOL. I had enough fun trying to weld Cru Forge to 15N20 and 416, so I know what you mean.

From my experience trying to weld 1.2442 to 15N20, I would agree with you wholeheartedly. I stopped one fold before I wanted to because that stuff just didn't want to move easily!!!!!:soapbox:

Why, Mr. Blue, are you implying that those two steels might not be so easy to weld up? :shrug:;)

Not surprising. I have said in the past that 1.2442 on paper resembles Hitachi Blue #2 but with a slightly different carbon content and perhaps even more tungsten. I have some 1.2442 left and I also...

It seems to me that the combination of those two steels would give you very high fine edge stability like they do when used by themselves. Razor people sure love that. My question is does the...

Very nice, Gabor. I am not always a fan of sapwood in ironwood, but you used it in a very eye pleasing way with these scales. At first glance, it almost looked like you had done an inlay. I know that...