i like your thinking, i think it wouldnt be a bad idea to do this HT though a torch... im not too worried about the spine since its mild steel so im with spaz on that unless im missing something......

thats exactly what i remember from the story, is they did it in the forge and watched for that and right when it hit quenched... i only have a kiln.... if this was just a regular piece i wouldnt be...

i accidentally started to final grind a blade when i realized that i hadn't done the heat treatment on it done hahaha right now the thickenss of the edge is down to .5mm thick, it is a wedge so its...