Yeah, I meant to clarify that it mainly applies (as far as I know) to a steel that has a tendency to have retained Austenite after heat treatment. I just wanted to make the point that it could be...

There is a small difference between using one temper cycle versus two or three: any Retained Au,stenite is converted to Martensite during the cooling after the blade is heated to tempering...