i have parks 50 also and it great stuff. i cover...
i have parks 50 also and it great stuff. i cover all my oil hardening stuff (slow oil steels i interrupt the quench) that and the Al plates for quench of air harding steels is mostly uneventful
... -
05-18-2008, 01:33 AM
Thread: Blade Steel types for razors
by L R Harner- Replies
- 36
- Views
- 11,736
what do you use for quench and what temp did you...
what do you use for quench and what temp did you quench from. thats the big 2 trouble shooing not gettign hard
now that said do you know for sure what the Damascus has in it (some have been known... -
05-16-2008, 02:32 PM
Thread: Blade Steel types for razors
by L R Harner- Replies
- 36
- Views
- 11,736
i was planning on going to 52100 but found a good...
i was planning on going to 52100 but found a good source of W2 (40lb) for now that will be my razor stock
now this said i have a computer controlled kiln and LN dewer and parks 50 for my heat... -
05-15-2008, 03:45 PM
Thread: Blade Steel types for razors
by L R Harner- Replies
- 36
- Views
- 11,736
i plan on a gass set up too when i can get the...
i plan on a gass set up too when i can get the space in the shop for it
but any how lots of different ways to mess the steel up a bit
so get known steel learn all you can about it and take your... -
05-15-2008, 03:04 AM
Thread: Blade Steel types for razors
by L R Harner- Replies
- 36
- Views
- 11,736
and if you don't know what your doing at the...
and if you don't know what your doing at the forge you can reallyl hurt the steel
try that on a grinder (white hot and sparking :) )
right now i know im more prone to mess ups at the forge then i... -
05-13-2008, 04:35 AM
Thread: Blade Steel types for razors
by L R Harner- Replies
- 36
- Views
- 11,736
from what i recall you would want to use nothing...
from what i recall you would want to use nothing 1060 or less
but anything bigger 10XX wise should be fine
the key here being know your heat treat info ok steel with great heat treat is still...