05-10-2010, 02:31 PM
Thread: Blademeisters: Bellied Hollow?
by L R Harner- Replies
- 22
- Views
- 4,969
i have some of don hansons W2 that i plan on...
i have some of don hansons W2 that i plan on using also have been told that parks 50 is safer then water and about 90% as good
-
05-05-2010, 10:19 PM
Thread: Blademeisters: Bellied Hollow?
by L R Harner- Replies
- 22
- Views
- 4,969
thanks but that blade is plane jane i will try...
thanks but that blade is plane jane
i will try and get some more crazy action on the clay that was jsut a test -
05-05-2010, 07:17 PM
Thread: Blademeisters: Bellied Hollow?
by L R Harner- Replies
- 22
- Views
- 4,969
in the knife world if you have a soft core in...
in the knife world if you have a soft core in steel less then 3/16 thick your hardening wrong(or making a quench line )
from quench the steel will be 65-67 hardness and brittle then a temper temp... -
05-05-2010, 03:25 PM
Thread: Blademeisters: Bellied Hollow?
by L R Harner- Replies
- 22
- Views
- 4,969
here is what a 3 wheel grind would look like if...
here is what a 3 wheel grind would look like if you didnt smooth out the bumps
-
05-05-2010, 03:14 PM
Thread: Blademeisters: Bellied Hollow?
by L R Harner- Replies
- 22
- Views
- 4,969
the "soft center" would be more from bad quench...
the "soft center" would be more from bad quench not from botched temper
some steels are shallow hardening (but still more then and 1/8 inch deep ) when done right
when you temper you may have...