You shouldn't mix pastes on one surface, because...
You shouldn't mix pastes on one surface, because you never know what the result will be. You can get chromium .5 at handamerican.com.
-
10-27-2006, 01:49 AM
Thread: Which pastes would you use?
by Joe Lerch- Replies
- 22
- Views
- 2,592
That's not what I meant. I only mentioned 100...
That's not what I meant. I only mentioned 100 passes because Randy said he did that in a recent post. But you got the idea. If you go to .5 too soon you'll have a lot of work, and it can get...
-
10-26-2006, 11:32 PM
Thread: Which pastes would you use?
by Joe Lerch- Replies
- 22
- Views
- 2,592
Hey, you can do anything. But you'll need a lot...
Hey, you can do anything. But you'll need a lot more roundtrips on the .5 if you skip the 1 micron.
Randy thinks nothing of doing a 100 roundtrips. That tries my patience. I don't need that... -
10-26-2006, 11:27 PM
Thread: Which pastes would you use?
by Joe Lerch- Replies
- 22
- Views
- 2,592
I would go for 1 and .5 microns. That gives you...
I would go for 1 and .5 microns. That gives you about 15K and 50K. It's not a bad transition and the .5 will leave the edge beautiful.
As for keeping off the hone, the way you do that is by...