I noticed most have air flow source as some sort of blower, I'm using an air compressor at 100 - 120 pounds blowing thru a water heater burner bolted to botton of a wok.

[QUOTE=Bruno;
Basically, when you heat treat 1095, you have a second or so to drop the temperature. If you don't cool down that fast, your 1095 will still be soft enough to bend.
So logically, if...

I am using 1095

203843[QUOTE=Mike Blue;1507787]How high was your austentizing temperature before annealing? Please list what you did in your annealing process. QUOTE]

Do not know temp as I just heated in a...

In my first attempt i tried stock grinding to the perfered shape. I would like to try to forge one. I have gotten to the desired basic shape but want to know if I wasted time of annealing before...