Hey all,
I got a disinfectant from the same place I purchased my only new SR, as I wanted to clean all the ones I got off Ebay. However, when I used it, all the blades went all speckled and stained and this will not come off at least by using a dremel with a buffing wheel.
Attachment 110136
The blade in the picture was of a mirror shine when I got it, but looks absolutely horrible now.
Any suggestions on saving these?
Best,
Dave
Did you use any polishing compound ? I have used mothers metal polish and have gotten good results. I have also heard Maas is good just don't get it on any gold wash it will take the gold off.
Didn't use any polishing compund, as a) I didn't have any here, and b) I didn't want to wreck them even more. I'll try to check with the locals (Swedes) here on SRP on what's available here. Thanks.
Any good metal polish that's safe for chrome will work; if that doesn't get it off....break out the sand paper :eek: What kind of disinfectant was it?
I still think either alcohol or a multisurface (safe for glass) natural bathroom cleaner works the best without having to worry about damaging the steel or finish. There was a thread about a month ago where a guy didn't dilute barbicide and he now has some pretty blue cracked ice dubl duck scales :p
What type of disinfectant was it?
So, I got some metal polish (safe for Chrome). (Häxans, for all you swedes.) I followed the instructions, and the blade became shiny, but the staining is still there. Much annoyance ensued.
The disinfectant was a no-name ordered from Gents.se, in tablet form. The tablet gives 5 litres of disinfectant, and 8 stained blades. (Ok, so that last part wasn't in the marketing.)
Thanks for all the input guys, and if you have any magic "make-shiny-again"-tips, I'll happily listen. I'm loathe to break out the sand paper. :-/ Goo thing I didn't clean *all* my blades.
That "staining" could be very minor surface pitting that polish won't get out. You could try wet sanding very very lightly with 2000 or higher grit sandpaper and see if that removes it...again, very very lightly just to test one blade.
Thanks for the tip about pellet blade cleaner!
The more I look at the first blade shown with the spotting and pitting, the more I think of intergranular corrosion. The fine fogging usually is a give away. I would do a quick honing at 600grit to 1K or less and look at the blade under 60X or more and you may see holes through the bevel. When I get one that bad, I don't want to waste my time trying to get an edge. That corrosion pattern is what I expect from a celluloid rotting acid on a blade.
I may be wrong and I won't say the blade is bad; look for signs of re-scaling.
~Richard
Why would you even consider disinfecting a blade with anything so aggressive? All I do with used blades is buff them up and wipe them down with alcohol, the alcohol will kill anything the buffing did not remove. If you're still worried a dip in boiling water will kill anything and not harm the blade (careful with scales though).
I hope you will not find hard way that alcohol does not kill everything.
Best to use a barber type disenfectant . Barbercide or HYDROCIDE . But follow the instruction. No longer than it says. And not on the scales unless your sure what they are. Wood, bone, horn Etc. be real careful.
Hi derman. I can tell about disinfection that stains metal. If it contains iodine it will stain your blade. I had an accident with one of my blades and wiped it of with "jodopax" solved in water. It gave my blade a red tone. I have read about this on different forums and it seems almost impossible to remove.
If you find a solution, please tell us.
PS. Jodopax is a solution for disinfection on animals, mostly used on horses in Sweden.
I think you are looking at a simple case of rust, many strong disinfectants intended for dilution contain sodium hydroxide (caustic soda) which will cause rapid oxidization.
I saw a similar tho less extreme case recently when i wiped down some restored blades with a new disinfectant before shipping them to their new owners. I was horrified to find they all had light pitting the next day when i went to wrap them up! I was lucky as it was light enough to remove with metal polish. Looking at your blade i think you you're going to have to have to go at with wet'n'dry.
So,
I managed to get rid of the staining, by using Autosol. Worked like a charm! Thanks for all the help guys!:rock: