Thread: Refinement of the cutting edge

I meant how bad the edge gets after the shave.

What is your final finsihing stone?

Yes, it's happened to me, but with a twist: shave feels like the razor isn't quite there, but plow through it anyway only to finish and my face is just as smooth as if I'd used any other sharp blade - with no irritation the next day! I haven't done enough experiments on edge longevity, though subsequent shaves with these razors seem to yield the same results.

Sorry Kees, I can't comment on your specific issues other to suggest some additional light finishing strokes, but even that seems to be a fine line. Too many and the edge seems to get fragile. Oh well, like the saying goes "less is more"....

Originally Posted by Ryan82

Yes, it's happened to me, but with a twist: shave feels like the razor isn't quite there, but plow through it anyway only to finish and my face is just as smooth as if I'd used any other sharp blade - with no irritation the next day! I haven't done enough experiments on edge longevity, though subsequent shaves with these razors seem to yield the same results.

Ver accurate description of the situation.

Final polisher: Hohenzollern (very similar to Y/G Escher, probably a tad finer).

Originally Posted by Kees

Final polisher: Hohenzollern (very similar to Y/G Escher, probably a tad finer).

I thought you used naturals. You have too many beautiful finishers my friend. That’s an extremely fine stone.. I am not saying you have done this, but I have had similar issues occur when using ultra-fine finishing stones by over honing the edge. Especially on certain razors. I learned I was applying too much pressure at this final stage of finishing.

Half my face would shave great WTG, and then the shave declined the rest of the shave. When I observed the edge under 100X magnification I could see the edge was peeled over like foil intermittently along the edge. I would then go back to 8000 grit and work back up.

If this is isolated to just the two razors it could be a steel temper issue. Go back to 8000 grit and inspect edge progression under magnification. If the edge is still breaking down I would try a layer or two of tape at 8000 grit level and repeat progression. See what happens.
Mike

Razors are not overhoned. I'll take them to the 5K Shapton followed by the Hohenzollern and see what happens.

Originally Posted by holli4pirating

I meant how bad the edge gets after the shave.

Dunno, I repolish edge before it hits my face again.