Thread: Heat Treatment on a thin edge

On the 1095 ttt diagram it looks like the top of the curve is about at 1375, so if you hit the quench after cooling down to 1400 everything should be fine and you will beat the nose of the curve if you are fast enough.

I have done this with both my kiln and in a forge. Speaking from experience, my biggest problems with thin blades has been warping not beating the nose of the curve.