    Default 01 tool steel grind

    i have a piece of tool steel that im making a big razor with, and it will be a wedge with a top of 3/8 inch wide and a hieght of 2 inches. my question is, when im grinding out the wedge, how thin can i get it at the bottom without it warping during heat treatment

  2. #2
    Senior Member justinA's Avatar
    Join Date
    Oct 2011
    Location
    livermore, ca
    Posts
    210
    Thanked: 15

    Default

    Height of 2", as in 16/8?

  3. #3
    Heat it and beat it Bruno's Avatar
    Join Date
    Nov 2006
    Location
    Belgium
    Posts
    15,130
    Thanked: 5229
    Blog Entries
    10

    Default

    You should have at least 1/16th thickness left if you want to be reasonably safe.
    Til shade is gone, til water is gone, Into the shadow with teeth bared, screaming defiance with the last breath.
    To spit in Sightblinder’s eye on the Last Day

  4. #4
    Junior Member
    Join Date
    Dec 2011
    Posts
    14
    Thanked: 0

    Default

    yes justinA,.... 16/8

  5. #5
    "My words are of iron..."
    Join Date
    Oct 2006
    Posts
    1,898
    Thanked: 995

    Default

    Quote Originally Posted by Bruno View Post
    You should have at least 1/16th thickness left if you want to be reasonably safe.
    +1 Heat treatment of steel is a violent and dynamic process. The potential for movement of the steel (curve or warp or twist) always haunts the blade maker no matter how well planned to prevent it. Leave a thick enough edge that if you do get a little warpage you can see a straight line down the middle.

    There are already a great many techniques discussed here for correcting warps on hones during restoration. The process on a new razor from new stock would be identical. You will have to remove some superficial material to polish the razor after heat treatment as there are always oxides of some kind. It means you have to be careful to grind/polish away that along with the excess edge material and keep the blade cool so as to not ruin the heat treatment. Thin steel heats very quickly.

    Look forward to the mistakes. They are the best teachers. As you gain experience, you may find you can reduce the edge thickness to less than a sixteenth, but it's a safe place to begin.
    ScottGoodman, jeness and 32t like this.
    “Nothing discloses real character like the use of power. Most people can bear adversity. But if you wish to know what a man really is, give him power.” R.G.Ingersoll

  6. #6
    Junior Member
    Join Date
    Dec 2011
    Posts
    14
    Thanked: 0

    Default

    thanks mike. i was wondering if it was possible to rig a frame that would hold the blade and keep it from bending. also, is their an optimal way to quench it, ie, blade side going in first, tang side? or straight down from the front

  7. #7
    Heat it and beat it Bruno's Avatar
    Join Date
    Nov 2006
    Location
    Belgium
    Posts
    15,130
    Thanked: 5229
    Blog Entries
    10

    Default

    That is possible, but as a consequence, the part that is covered by the frame would not be hardened.
    Gilette thought of the same thing to prevent his DE blades from warping. But DEs don't have a spine or a big body.
    If the spine is softer than the edge, it will wear faster too.

    Besides, there is still the possibility that the spine or entire blade will warp ever so slightly. It is a big chunk of steel. If that is contracting asymmetrically, no simple jig will keep it straight. Now, it won't warp overly much, but if you've already ground it very thin, it is possible that you don't have enough material left to grind a straight edge out of.
    Last edited by Bruno; 01-11-2012 at 07:32 PM.
    Til shade is gone, til water is gone, Into the shadow with teeth bared, screaming defiance with the last breath.
    To spit in Sightblinder’s eye on the Last Day

  8. #8
    "My words are of iron..."
    Join Date
    Oct 2006
    Posts
    1,898
    Thanked: 995

    Default

    I just plunge them in toe end first. One quick move. Most of the jigs or frames I'm aware of, are for steels that are air cooled or have a much longer time available between the austenitizing/critical temperature and the quench.

    O-1 for example gives you about two seconds to get from the heat to the quench and then below 1000 F to start to have the potential to form martensite and below 325 F for 100% martensite. Beating the nose of the curve is the most critical component. See here: Steels and scroll down to see the TTT diagram for O-1. Once you're past 1000 F you have a nice relatively leisurely amount of time to drop to 325 F. But those first two seconds are important.
    32t and gregg71 like this.
    “Nothing discloses real character like the use of power. Most people can bear adversity. But if you wish to know what a man really is, give him power.” R.G.Ingersoll

  9. The Following User Says Thank You to Mike Blue For This Useful Post:

    Str8Raz0r (01-12-2012)

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts
  •