Thread: What actually is Hardness in natural stones, and how it affects sharpening

I have followed the Shoobie Doobie Asagi thread with great interest for weeks now, very nice stones shown here and there throughout and that thread as developed some great off topics. The topic of Hardness in Natual stones is universal and I do have some opinions about how it affects sharpeing that I would like to explore.

Sharpening is the act of removing steel, it is a grinding process that is used to create a geometrical profile to a blade. If a stone is not grinding it is not sharpening, period.

The hardness of a stone is the action at the stones very surface and it is all about the stones ability to shed particles from the stones surface during the sharpening process, period. All stones are hard, but their relative softness might be important also as an attribute.

I think it is overly complicated to merge synthetic stones and natural stone together in the discussion of natural stones, but to not recognize that some synthetic stones are hard or not is helpful in part because we here on this forum do use some of the same synthetics as others here do, so their names and numbers can be a jumping off point. But that is about as far as it goes in my opinion.

I know that some members would like to know if all Nakayama stones are harder than Ohira. This is not really a question with a logical answer as many will agree. Each natural stone is unique in itself, and even within one mine, any given strata will provide a wide varity of stone characteristics and hardness is one component that can vary slightly. And I further suggest that within any one mines history, the hardness of the stone mined can vary for particular reasons from one decade to another.

The hardness of a stone and a stones cutting abilities are related.

On the hardness side, if a stone does not shed dulled used grit particles, but instead retains those as bound up dulled grit particles on the surface, this is when the stones cutting speed begins to decrease and eventually halts. When it halts the cutting action, the stone action will only be that of polishing the blade, a burnishing effect, it will not continue to grind or remove steel. This is fine if you want a polished blade that looks shiny. As the glazing of the stone progresses I will suggest that the stone will continue to cut steel but with ever decreasing efficency and there will be a point in time when the cutting action actually stops. If you continue to rub the blade on the stone after this point other factors come into play as far as the metallurgy is concerned.

On the stones cutting abilities side, it must be recognized that not all stones are created equal, and as measured per weight some stones have a greater amount (per pound) of grit particles verses binder clays, while some stones on the other hand have less grit and a greater amount per pound of binder clays. The stone with more grit per pound will always have more cutting power if all other things are equal like surface hardness, grit size, etc.

If you an scratch a stone with a tool this is a crude type of proof of the hardness, the stone has in fact shedded grit particles. Incorporating a given force upon a tool with given and known characteristics, this simple test on a stone could be useful in rating stones as having a certain hardness. The closest entity we have on this forum to conduct this test are the various descriptions of hand pressure, and various qualities of tool steel in the from or shaving razors. This is a start. Alx

the way i look at hardness is through density the more compacted the stone is the hard the stone will be the harder the stone the less of a cutter but it will be a better polisher

trust me, it is not that simple

Sharpening is the act of removing steel, it is a grinding process that is used to create a geometrical profile to a blade

That is right, but what about polishing? There is evidence that at high grit ratings, the grinding action (ie. removing steel) gets less important.
Tha major action here is a plastic deformation, rather than grinding (even though always both is present). Grinding per definition involves removing metal at a fast pace,
wich is hardly what we want to do. I would suggest reading some of this, b/c we always think there is so little knowledge about sharpening
but indeed there is. But it is disguised

Grind - Wikipedia, the free encyclopedia
Polishing - Wikipedia, the free encyclopedia

and heres something reall special, quite in depth theory of the difference in polishing and grinding
Metallography, principles and practice - Google Books

And heres another one about polishing mechanisms
http://www.asminternational.org/cont...85G_Sample.pdf

The hardness of a stone and a stones cutting abilities are related

Maybe, but there are many exceptions to that rule. Not only is "hardness of a stone" still undefined,
but what I would call a very hard synthetic stone (the shaptons, 16000 or 30000 for example, or the pro 12000) may be extremely quick
at removing scratch patterns and cutting microbevels etc. The Shapton 16.000 is staggeringly quick and can (not should) be used after the Cerax 6.000 with a couple of circles.

My Shoubudani is it appears to me a harder stone than my Nakayama Kiita.
But it also appears to me that it is quicker.

So my prediction is that there won´t be any consens about what is hardness and how does it affect a stones performance.
There is too much to take into consideration

I have very little definitive knowledge about this topic. What little I know comes from a barber in Newark, NJ nearly 30 years ago, and my own hands on honing since then. He told me, when selling me a coticule, that the best razor hones are softer than harder. They would cut faster if they were soft, and you could tell if you dug into the edge of the coticule with your thumbnail and it left a mark.

Of course we can watch our water and see if the stone develops slurry merely from the honing action, or if we have generated a slurry with a slurry stone, how quickly the slurry turns color. This gives some indication of the speed of the stone's cutting power. I have tried the thumbnail test on a coticule or two but it doesn't really work for me. Is the mark I'm leaving caused by the coticule cutting my thumbnail or my thumbnail cutting the coticule ? Anyhow ....

Then a couple of years ago I saw a yellow green Escher with two end labels. The first was the familiar "gelbgruhn", meaning yellow-green, and the opposite end had a label reading "guaranteed soft". I was very excited by this and was lucky to acquire the stone.

I already had the same stone without the guaranteed end label so after testing the stone and finding it equaled my y/g I sold it to finance some other craziness. I later regretted selling it, you can't have too many Eschers, and lo and behold lightning struck twice .... I found and acquired another.

So forgive me for cluttering your thread with photos of my prize, but I promised a friend to show some photos of it, and this is an ideal thread to insert them in. Note the last photo. There is part of an ink stamp on the honing surface indicating to me that the stone has never been used. A condition that I intend to remedy sooner than later.

lesslemming you are right about there is alot to consider when it come to stones when i think of hardness i try to keep it simple and think of density most of the time but not all of the time the harder the stone the slower it cuts but hardness has nothing to do with speed of cutting its what the stone is made of the "cutting agent" (and speaking of only natural stones because synthetic's are a different animal) take the ark stones their made of microcrystalline quartz once you start honing on the stone the quartz wears down flat it doesnt break apart it gets smooth and flat jnats are the completely different you could have two jnats from the same mine same hardness one having su and one w/o the one with su will cut faster like you said its alot to think about

Alex, thnx for the post.

Could you explain why some very hard stones
still have very good cutting abilities whereas
other hard stones are very slow? I know you
wrote that depends on grit per pound, but
what affects this?

The scratch test makes sense.

Basically what I would do, is I would hold the stone
in my hand to check its weight/density. Then I would
knock on the stone to listen what kind of sound it makes.
I assume a soft stone would make a duller,lower sound
whereas harder stones a more ''ping'', higer pitched sound.
Next thing I would do is sharpen on the stone, if I feel that
the surface of the stone is very hard(indentation wise, no
scratching ability), then I would think ''man this thing is like
glass!'' and conclude this is a hard/very hard stone.

Sharpman

Originally Posted by Lesslemming

Maybe, but there are many exceptions to that rule. Not only is "hardness of a stone" still undefined,
but what I would call a very hard synthetic stone (the shaptons, 16000 or 30000 for example, or the pro 12000) may be extremely quick
at removing scratch patterns and cutting microbevels etc. The Shapton 16.000 is staggeringly quick and can (not should) be used after the Cerax 6.000 with a couple of circles.

Yes, but the Shaptons are synthetic stones. They are still quick,despite being
hard, because they are loaded with grit particles. If a fine and hard stone is very
quick that either means the particles are very hard(think diamond)or the stone
has a lot of sharpening particles per square unit or both. Might be wrong though.

Sharpman

Originally Posted by SharpMan

Alex, thnx for the post.

Could you explain why some very hard stones
still have very good cutting abilities whereas
other hard stones are very slow? I know you
wrote that depends on grit per pound, but
what affects this?

The scratch test makes sense.

Basically what I would do, is I would hold the stone
in my hand to check its weight/density. Then I would
knock on the stone to listen what kind of sound it makes.
I assume a soft stone would make a duller,lower sound
whereas harder stones a more ''ping'', higer pitched sound.
Next thing I would do is sharpen on the stone, if I feel that
the surface of the stone is very hard(indentation wise, no
scratching ability), then I would think ''man this thing is like
glass!'' and conclude this is a hard/very hard stone.

Sharpman

checking for hardness do the water test put one drop of water on a few of your hardest stones which ever stone holds the water the longest is the hardest

Jimmy,

That stone is amazing, you really are lucky to find one that NOS. The one I have from you is amazing, I love it, I hug it in my sleep at night.

Originally Posted by eleblu05

checking for hardness do the water test put one drop of water on a few of your hardest stones which ever stone holds the water the longest is the hardest

Wouldn't holding water longer be a matter of density ?

BTW, my posting the Escher seen above, within this thread, was due to the label "guaranteed soft." I think the relevance to this thread is demonstrated by Escher finding guaranteeing softness for a razor hone, which is what Eschers were/are, an important enough selling point to print and apply a special label noting that characteristic.