Thread: Japanese naturals - Finishing question

Originally Posted by Brighty83

Yeah, that slurry looks familiar! I have quite a few stones that have that same slurry.

The slurry starts off grey tho, so something happens to change it to brown.

The suita is a fast cutter, it not a finisher although I can still shave off it. I've used it for a few knives and it gives my knives a razor edge It produces a brown\black slurry quite quickly.
To generalise. They are usually fast.

This Okunomon Suita has almost the same characteristics.
Im guessing these would produce the same slurry\preform much the same as your Okudo Suita except your stone is probably a little harder?
Yeah maybe. Couldn't say without using your stones

............

There is a huge difference between etching, pH and rust.
First of all, about rust; The easiest way to interpret this is, particles of rust inside the stone. Could be the way they came out of the earth, or it could be because someone used the stone for honing and forgot to clean it. It rusted, particles went inside the stone. Rust is a catalyst for more rust. If it was clean, nothing would happen, for a short time. But a single molecule, and bad things happen fast.
The finer the powder i.e. slurry, the faster it happens. And, when it happens, more rust is absorbed from the stone. So, keep your stones clean.
About the acid, the rock can't have acidic nature. Stones have been used with soda powder in their water for many decades. If the stone was acidic, we would most certainly know it by now from, including but not limited to, bubbles that come from the reaction. Or explosions and poisonous gasses or something. Insoluble acidic minerals are quite rare, and in most cases carbon dioxide is the (weak) "acid", next to a strong base with limited solubility. On the other hand, basic minerals are extremely common. Silicon oxide is also an acid. Again, pretty weak acid, and insoluble. But reacts with strong bases.
If the stone was acidic, the rust would be the last thing to worry about.
And, for the etching, are you sure it's not a polishing effect? I have seen many cool ones, depending the abrasive and what it contains.
I've been reading the thread for a while, so, those are my two cents, good luck.