Not to diverge from the topic and get into a metallurgy argument but I'll have to respectfully disagree. O1 can easily be overheated which cause grain growth blah blah blah. Its best done in a...

Since your planning on doing your own HT, (if your buying stock, which is the best route to go IMO, mystery steel can work sometimes, and sometimes you just get a hunk of metal that doesn't perform),...