A quick note on the cryo. Oh, I have the flu, and...
A quick note on the cryo. Oh, I have the flu, and my brain is jello... Please forgive me if this doesn't make any sense.
For O-1 steel, cryo. treatment is not needed and is usually a unnecessary... -
04-12-2013, 06:11 PM
- Replies
- 35
- Views
- 3,995
Salt at 1490F is used to heat the blade. It is...
Salt at 1490F is used to heat the blade. It is great for protecting the surface of the steel from oxidation, very even heating, and precise temperature control.
A different salt, at 375F - 450F,... -
04-12-2013, 06:05 PM
- Replies
- 35
- Views
- 3,995
If you're after Banite, as opposed to Martensite,...
If you're after Banite, as opposed to Martensite, that will work.
-
04-12-2013, 05:26 PM
- Replies
- 35
- Views
- 3,995
First, the blade must be properly normalized and...
First, the blade must be properly normalized and spherodize annealed. Then,
If using a gas forge, for O-1:
1. Heat to 1500F - All "shadows" are gone. No soak at temperature. It is too easy to...