I'm thinking Laurens has it right but I would first hone the edge to see if it will take a good edge. You never know what is under those dark spots near the edge. If it takes a good edge and the metal is not Swiss cheesed under those dark spots you won't be wasting your time restoring it. I would bet it is just fine but you never know.

Bob