06-21-2016, 01:41 AM #1
To sand or not to sand...
Hello Gents,
I have this Imperial that I had been in search of for a while and am now getting around to working on it. There is some pretty harsh pitting but the etching is still in great shape. I have only done a mild clean up (WD-40, 000 steel wool, Mothers and a rag). Not sure if I want to sand it but I do want the etching to come back to life. What would you do? I do not mind pitting on an old razor as long as it is clean and not rusting anymore. I am just second guessing how far I want to take this clean up.
Bad pics I know
Tonight's pic
As you can see, it has pitting.
Thank YouJohn
-
06-21-2016, 01:57 AM #2
The first thing I would do is take it to a 1K [Insert brand here] with tape and see how the pitting near the bevel cleans up before deciding anything else.
-
The Following User Says Thank You to 32t For This Useful Post:
jwy77 (06-21-2016)
-
06-21-2016, 02:17 AM #3
For the next little while tonight I am going to work on the edge. I have looked at it through a 60x loupe and it needs a bevel set. It has been honed poorly before and stored poorly after that. At least I didn't pay too much for it. I really like Imperials the others that I have took a great edge and hold them well, this is the worst shape I have started with.
John
-
06-21-2016, 02:36 AM #4
- Join Date
- Apr 2008
- Location
- Saint Paul, Minnesota, United States
- Posts
- 2,943
Thanked: 433Really cool etch! I wouldn't go much further maybe 1000 sandpaper. I wouldn't go much lower.
As 32T said, make sure the edge is ok before going much further
-
The Following User Says Thank You to rodb For This Useful Post:
jwy77 (06-21-2016)
-
06-21-2016, 02:51 AM #5
I have never seen an etch like that, nice find! Do some poking around here and you can find some great threads on preserving etches by people far more skilled than myself If I restoring and want to keep an etch I will usually just do a rough clean so I don't risk removing it.
Good luck, and post pictures of the finished product!
-
06-21-2016, 02:55 AM #6
I'll go out on a limb and say that the edge will be fine.
I'll also say that I'd start with just some metal polish/Mothers Mag and Aluminum is my go to. You can always go coarser but once you do, it takes a lot of work and steel to go back up
Perhaps it's just the pic but there seems to be a problem at the heel. The Red shows the general area and the Blue shows the area in question.
Just an observation/I hope its of some help.Our house is as Neil left it- an Aladdin’s cave of 'stuff'.
Kim X
-
06-21-2016, 03:46 AM #7
Yes it does have some issues on the heel, well it has some issues everywhere but the heel has a chip. That chip is far enough from the edge to make me think to just leave it alone. After some work on a Naniwa 1000 Professional, the bevel seems to be ok. Still needs work though.
John
-
06-28-2016, 12:41 AM #8
- Join Date
- Jun 2016
- Posts
- 8
Thanked: 0Hi, First time user of the forum,I hope I'm posting in the proper place, the etching is amazing, I would love to find a blade with anything cycling related. Yesterday I purchased 2 SR second hand, I don't have very muck knowledge on the pieces,I am afraid of losing (sanding) the hallmarks,stamps and engraving off the blades, basically I don't know where to begin, the edges feel and looks to be in shave ready (from what I can tell) any help or advice would be greatly appreciated,Best of luck on your beauty and hope everything turns out well. Thank you in advance.
-
06-28-2016, 12:49 AM #9
Welcome from SE Washington State USA,
Pictures are almost a MUST! Please include some if at all possible.
Again Welcome!
Our house is as Neil left it- an Aladdin’s cave of 'stuff'.
Kim X
-
06-28-2016, 08:15 AM #10
- Join Date
- Jun 2016
- Posts
- 8
Thanked: 0Thank you, I am still trying to figure out some of the attachments on the form at the moment I only have access to a iPhone, I hope the pictures made it and thank you again