Excellent! Thank you again Richard.

Though it presents the need for more work, I tend to like symmetry.. so an equal inlay on each side..?

Does anyone have the temperature that horn becomes plasticized? And then what range do we have to work with before it is too soft and/or begins to burn or bubble?

Not that it would be necessary.. but a laser temp reader might be handy in that regard.