I watched your grinding video. I have a couple suggestions. It will help if you grind the edge thickness to about 0.7mm before heat treatment. This leaves a lot less to remove when the steel is hard.

After heat treatment, slow your belt sander way down, and grind with the belt wet. This will preserve the temper of the steel.

I hope this helps.