In my mind, Ice hardening means cryo tempering.

Because if you quench a steel in ice, it will probably crack.

As for cryo temp itself, you normally give it a snap tempering (quick and not too hot IIRC), then cryo, then "normal" tempering.

To resume: Don't do it on an already Heat Treated blade.