Quote Originally Posted by falingore View Post
Also, side note, I hadn't expected the copper-plating. It makes sense now, but is something I hadn't considered at all last night.
Kit, Ohm's law is way over my head!!! I am certainly glad you are here to help explain some of the technical aspects of this process. I can only report what I visually see and can measure with a multimeter. I will defer to you to explain to the members what is happening technically. Have you considered testing your theory? That is, take the razor out once the amperage drops and take pictures. Put it back in the same vat and continue the process for 24 hours and see if there is any difference? That might tell us if you theory is correct. Oh, and by the way, I guess you don't need any help from me to use a multimeter.

Will you explain why the copper-plating makes sense to you? It would have been the last thing in the world I would have expected to happen and I still do know understand why it did. Can we use this process for electroplating the blades???

Have fun and be safe.

Randy