Thread: Need Help with a C-MON/FILA restore

Fine sandpaper and lots of rubbing. You seem to have some slashes from lower grits still, so stay with the finer stuff, up and down.
The wet/dry and WD40 seems to work best. You have come a long way! It will be worth it!

the progress is looking really good, I'm with the others and think hand sanding is best. I might just be saying that because I don't have a lot of buffer experience, so it makes me extra careful about when to stop buffing. I may also cry if I messed up that blade. I mostly hand sand and actually use the buffer very little. You can work the last little bit of black out with steel wool and polish, it does leave the pits because it doesn't remove the steel. I did mess up an extra hollow hand sanding too, you can still go to thin. Some blades don't really have a lot extra to play with.

You have to use the force Luke :<0) If your worried about going to far then stop with the heavy grits. The lengthwise lines have got to go but I would use as light a grit as you can going up and down the blade. Doing little circles with the next fine grit to make sure you got alllll the previous grit marks out. I find those length wise scratches harder to get out for some reason so I avoid those strokes after I am sure I have gone as far as I want with pit removal. They don't look so bad if you get all your scratches out. The finer grit you go to the easier to get to shiny which means less time on the buffer for that phase.

Originally Posted by 10Pups

You have to use the force Luke :<0) If your worried about going to far then stop with the heavy grits. The lengthwise lines have got to go but I would use as light a grit as you can going up and down the blade. Doing little circles with the next fine grit to make sure you got alllll the previous grit marks out. I find those length wise scratches harder to get out for some reason so I avoid those strokes after I am sure I have gone as far as I want with pit removal. They don't look so bad if you get all your scratches out. The finer grit you go to the easier to get to shiny which means less time on the buffer for that phase.

Thank-you Sir, I will do as you recommend.I appreciate you weighing in. I want to try shaving with this one first, then back to the workshop it goes. I couldnt ask for a better mentor. Oh Obe Wan . I must learn the way to shiny clean metal. The light saber sanding stick is been getting a work-out.

Originally Posted by 10Pups

You have to use the force Luke :<0) If your worried about going to far then stop with the heavy grits. The lengthwise lines have got to go but I would use as light a grit as you can going up and down the blade. Doing little circles with the next fine grit to make sure you got alllll the previous grit marks out. I find those length wise scratches harder to get out for some reason so I avoid those strokes after I am sure I have gone as far as I want with pit removal. They don't look so bad if you get all your scratches out. The finer grit you go to the easier to get to shiny which means less time on the buffer for that phase.

Same. Long, deep scratches are sometimes worse than the original corrosion.

Dave